is able to load harder as 7210 LS. The maximal loading is 3,00 N/mm². This mat will be used in areas, where other anti slip mats on SBR/NBR-base are not possible according the black colour.

Maximum loading
300 t/m² = 3,00 N/mm² by 8 mm thickness

slide adhesion factor µD
proofed by Fraunhofer IML. Different screen printing botoms from 26 mm thickness, EPAL euro-wood-palet, multible way,used .

Parallel to the skids µD = 0,85/0,85/0,87
lowest value = µD 0,85

cross to the skids µD = 0,94/0,88/0,90
lowest value = µD 0,88

lowest value total= µD 0,85

In addition in a DEKRA-Test was measured the situartion of 9510 RHS with paper coils. Result: 9510 RHS is available as safety part according VDI 2700 /9. If you need it, we can send the DEKRA-certifikate to you.

IT-GS do not annonce slide adhesion factors, what are not prooved. Because the slide adhesion factor of rubbing increased base is addicted form the used material copulation, the temperature, the condition of the material surfaces and the anti slip mat (dirt, wetness, and so on). To arrive the optimal slip inhibition, the contact areas, that means loading and bottom, have to be well swapt, clean, free of fat and dry.

Material: anti slip mat of Buthyl natural rubber

Colour: multi coloured

Area weight: approx. 7,36 kg/m² by 8 mm thickness

Volume weight: approx. 920 kg/m³

Tenacity: 0,85 N/mm² DIN 53571, Prüfkörper B

 

ultimate elongation: 105 % DIN 53571, proof body B


Temperature resistance: - 40 °C til 115 °C

Fire behavior: B2 DIN 4102

Stability
By having cracks, holes, crushes, contact with oil, gaz, chemicals and so on, 8012 LS cann´t used longer and have to be changed.

Stability
UV-light, sodium chloride, low acid and bases, (swelling by carbon hydride, like oil und gaz and more.).

Cleaning
shake out, suck, wash, may be with high pressure cleaner.

Recycling: waste key no. 070299
 
Delivery condition: rolls, plates, pre-cut according your wish

Thickness: 3 - 20 mm